Grade Tensile
Strength Mpa, (Min)		 Yield
Strength 
Mpa, (Min)		 %Age
Elongation
in 50mm
gauge length min		 Hardness (Max)
BHN Rb
301 515 205 40 217 95
304 515 205 40 201 92
304L 485 170 40 201 92
310S 515 205 40 217 95
316 515 205 40 217 95
316L 485 170 40 217 95
317 515 205 35 217 95
317L 515 205 40 217 95
321 515 205 40 217 95
347 515 205 40 201 92
409 380 170 20 179 88
409M 430 275 20 187 90
410S 415 205 22 183 89
410 450 205 20 217 89
420 700( max ) - 15 217 95
430 450 205 22 183 89
JSL AUS 515 205 40 217 95
JS- 203 515 205 40 217 95
301M 515 205 40 217
95

ASTM A403 WP904L Pipe Fittings Mechanical and Physical Properties

Typical Values at 68°F (20°C)

Grade Tensile Strength (MPa) min Yield Strength 0.2% Proof (MPa) min Elongation (% in 50mm) min Hardness
Rockwell B (HR B) Brinell (HB)
904L 490 220 36 70-90 typical 150
Grade Density
(kg/m3)		 Elastic Modulus
(GPa)		 Mean Co-eff of Thermal Expansion (µm/m/°C) Thermal Conductivity
(W/m.K)		 Specific Heat 0-100°C
(J/kg.K)		 Elec Resistivity
(nΩ.m)
0-100°C 0-315°C 0-538°C At 20°C At 500°C
904L 7900 190 15 - - 11.5 - 500 952
Werkstoff No 1.4401 Butt weld Pipe Fittings Mechanical Properties
Grade Density Melting Point Tensile Strength Yield Strength (0.2%Offset) Elongation
SS 316 8.0 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 316L 8.0 g/cm3 1399 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 316H 8.0 g/cm3 1400 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %
SS 316Ti 8.0 g/cm3 1399 °C (2550 °F) Psi – 75000 , MPa – 515 Psi – 30000 , MPa – 205 35 %